Page 4 - PET-G SHEETS

PET-G Sheet PET-G Sheet
Quantities Per Pallet Thickness PET-G Heating Times
According to Acrylic
Size Thickness Thickness 300.0
Thickness Tolerance 250.0
(2050 x 3050) (mm) (mm)
2 mm 75 pcs 2 ± 0,2 Heating Time (sec) 200.0
150.0
3 mm 50 pcs 3 ± 0,3 100.0
4 mm 37 pcs 4 ± 0,4 50.0

5 mm 30 pcs 5 ± 0,5 0.0
1 2 3 4 5 6 7 8 9
6 mm 25 pcs 6 ± 0,3 Sheet Thickness (mm)
8 mm 18 pcs 8 ± 0,4 PET-G XT - Acrylic Without Pre-Dried
Pre-Drying Acrylic
10 mm 15 pcs 10 ± 0,5

PET-G Heating Times
According to Polycarbonate
300.0
250.0
Heating Time (sec) 150.0
Elasticity Module Comparison Table 200.0
100% HI-PMMA 100.0

50% HI-PMMA 50.0
0.0
Polycarbonate 1 2 3 4 5 6 7 8 9
Sheet Thickness (mm)
PET-G
0 500 1000 1500 2000 2500 3000 3500 PET-G Polycarbonate Pre-Dried
W/O Pre-Driying Polycarbonate
MPa
ISO 178 Elasticity Modules - 3mm Sheet

PET-G Cycle Time
According to Acrylic
Impact Strength Comparison Table
300.0
100% HI-PMMA 250.0
50% HI-PMMA 200.0
@ -20°C Cycle Time (sec) 150.0
Cast Acrylic @ 23°C 100.0
Polycarbonate 50.0
0.0
PET-G 1 2 3 4 5 6 7 8 9
Sheet Thickness (mm)
0 20 40 60 80 100 120 140 160 180
Joules
ISO 6603-2 Impact Resistance - 6mm PET-G XT - Pre-Dried Pre-Dried
Sheet Acrylic Acrylic

Thermoforming Parameters Comparison

HI-PMMA PMMA-XT PET-G Polycarbonate
Sheet Temperature °C 160-190 170-190 130-160 190-210

Mould Temperature °C 60-75 60-85 35-55 100-140
Demoulding Tempature°C 55-85 65-100 30-60 80-120

Heating Time (4mm Sheet) (sec) 45 45 35 37
80 (Without Pre-Drying)
Cycyle Time (4mm Sheet) (sec) 110 95 95
67 (Pre-Drying)
4 | teknorm.com